Fiber-Plastic Composite dari Kertas Kardus dan Polietilena (PE) dengan Penambahan Maleat Anhidrida (MAH) dan Benzoil Peroksida (BP)
Abstract: The research
of utilizion corrugated
fiber and plastic
polyethylene as the
raw material of
making fiber plastic composite (FPC) board was useful to
give solution the waste problem. The purpose of research was to evaluate
physical properties (density, moisture
content, water absorbtion,
thickness swelling) and
mechanical properties (modulus
of elasticity, modulus of
rupture, internal bond,
screw holding power)
composite board of
fiber corrugated paper
and comparing the use of polyethylene plastic (PE) with maleic anhydride
as compatilizer and benxzoil peroxide as initiator and comparing
the physical and mechanical properties
FPC board wtih
testing the physical
and mechanical properties the composite
board were carried
out according to
JIS A 5905-2003
hardboard S20 dan
JIS A 5908
(2003) particleboards type 13.The result of the research showed that
physical the fiber plastic composite board did not fulfill the standard of JIS
A 5905-2003 hardboard S20, except density, water absorption and the thickness
swelling. The testing of mechanical properties did not fulfill standar JIS A
5905-2003 hardboard S20 dan JIS A 5908 (2003) particleboards type 13, except
internal bond and
screw holding power.
FPC board suitable
for using exterior
and interior, because
by on physis and mechanical
properties testing, the best value of fiber plastic composite was composition
60:40 MAH 5%.
Keywords: fiber corrugated
paper, polyethylene, fiber plastic composite, physiscal and mechanical
properties
Penulis: Rumondang Bulan
BatuBaraa, Luthfi Hakimb, Tito Suciptob
Kode Jurnal: jpkehutanandd130097