INVESTIGASI TEKANAN OPTIMAL PADA PROSES PRESSURED SINTERING KOMPOSIT PLASTIK HDPE-KARET

ABSTRACT:  The  purpose  of  the  research  is  to  investigate  the  optimum compaction of pressured sintering process for HDPE-rubber composite. The  raw  materials  used  are  HDPE  plastic  waste  of  oil  bottle  and  unused  tire. These  materials  were  powdered  via  mechanical  grinding  manually.  The  plastic powder  size  of  -60  mesh  was  selected  to  be  roled  for  specimen.  Pressured sintering  process  for  producing  the  specimens  was  done    at  120^oC    for  5 minutes. Parameter observed is the sintering pressure within range of 0,5 to 2 MPa  risen  0,5  MPa  incrementally.  Specimen  testing  involved  density,  bending strength  and  izot  impact  strength.  All  of  testing  was  conducted  on  ASTM standard testing. The result reveals that adding sintering pressured will increase density, flextural and impact strengths of about 14%, 52% and 17% respectively. The significant increasing properties occurs when the compaction reach to the optimum value, that is 1,5 MPa.

Keywords: powder technology, pressured sintering, density, particle bounding

Penulis: Heru Sukanto

Kode Jurnal: jptmesindd080021

Artikel Terkait :

Jp Teknik Mesin dd 2008

• ANALISIS PERFORMANSI PROTOTIPE PENGERING JAMUR KUPING DENGAN MEMANFAATKAN EFEK RUMAH KACA DAN ENERGI SUPLEMEN DARI BIOBRIKET LIMBAH LOG BAG
• Analisis perbandingan pemasangan sirip pada pipa bergetar terhadap perpindahan panas
• Laju pembuangan panas pada radiator dengan fluida campuran 80% air dan 20% RC pada rpm konstan
• Kajian eksperimental pengaruh tabung udara pada head tekanan pompa hidram
• Analisis struktur mikro lapisan bond coat NiAl thermal barrier coating (TBC) pada paduan logam berbasis Co
• Kontur tekanan dinamis pada permukaan atur sisi keluaran kaskade kompresor aksial bladetipis simetris dengan sudut serang bervariasi
• Pengeringan jamur dengan dehumidifier
• Pengaruh penggunaan pipa kondensat sebagai heat recovery pada basin type solar still terhadap efisiensi
• Rekayasa rancang bangun sistem pemindahan material otomatis dengan sistem elektro-pneumatik
• Pengaruh waktu pelapisan nikel pada tembaga dalam pelapisan khrom dekoratif terhadap tingkat kecerahan dan ketebalan lapisan
• Studi eksperimental orifice flow meterdengan variasi tebal dan posisi pengukuran beda tekanan aliran melintasi orifice plate
• Perhitungan aliran dan peramalan karakteristik pompa sentrifugal bertingkat dengan penggunaan CAD blade’s system
• Laju perambatan retak plat aluminium 2024 T3 dengan beban fatigue uniaksial pada rasio beban dan jarak diameter lubang berbeda
• Studi terhadap prestasi pompa hidraulik ram dengan variasi beban katup limbah
• Variasi berat roller sentrifugal Padacontinuosly variable transmission (CTV) terhadap kinerja traksi sepeda motor
• Pengaruh posisi pengelasan dan gerakan elektroda terhadap kekerasan hasil las baja JIS SSC 41
• Pengaruh besar arus pengelasandan kecepatan volume alir gas pada proses las GMAW terhadapketangguhan aluminium 5083
• Pengaruh massa air baku terhadap performansi sistem destilasi
• Kolektor surya jenis sirkular dengan memanfaatkan neon bekas sebagai kaca penutup
• ANALISA KONTAK ELASTIS ANTAR HEMISPHERES MENGGUNAKAN METODE ELEMEN HINGGA
• PENGEMBANGAN TEKNOLOGI RAPID PROTOTYPING UNTUK PEMBUATAN PRODUK-PRODUK MULTI MATERIAL
• APLIKASI LOGIKA FUZZY PADA PEMBUATAN PENJEJAK PANAS SATU SUMBU
• PENGUJIAN PERPINDAHAN PANAS KONVEKSI PADA HEAT SINK JENIS EXTRUDED
• PENGARUH WAKTU AUSTEMPERING TERHADAP SIFAT MEKANIS DAN STRUKTUR MIKRO AUSTEMPERED DUCTILE IRON NON PADUAN SERTA PADUAN Cu
• OPTIMASI JARAK ADJUSTMENT TENSIONING DEVICE PADA DRAG CHAIN CONVEYOR