Studi Cacat Lasan Pada Baja Struktural Dan Pencegahannya
Abstract: Cracked weld in a
construction is the beginning of more serious damage. Starting on fissure from
the cracked area on the heat affected zone of the connection joint and the
remaining tension in the material. Cracked weld can be divided in two groups
namely cold cracking and the hot cracking. Cold cracking was going on in the
weld beat at the temperature below the transformation temperature martensit
(Ms), about 300 oC. It may also occured not only onl HAZ, but also on the weld
metal. Hot cracking was going at the temperature above 550 oC. Hot cracking
devided into two classes, that is cracked due to loss restraints at heat
affected zone on 550-700oC, and also crack that occured at the temperature
above 900 oC at the time of weld metal solidification.
Penulis: Mulianti
Kode Jurnal: jptmesindd090188
Artikel Terkait :
Jp Teknik Mesin dd 2009
- PEMODELAN DAN SIMULASI SISTEM PEMBANGKIT TURBIN GAS PLTGU TANJUNG PRIOK
- PENGEMBANGAN ALGORITMA PEMBANGKITAN G-CODE MESIN PERKAKAS CNC OKUMA&HOWA BERFASILITAS AUTOMATIC TOOL CHANGER DAN INDEXING PADA SOFTWARE CaSTPro
- DEVELOPMENT OF AUTO-GENERATING AERODYNAMIC LOADS FOR WING-BOX FINITE ELEMENT MODEL BASED ON SCHRENK METHOD
- EVALUASI POLA FUNGSI RESPON FREKUENSI PADA RESPON GETARAN BANTALAN GELINDING
- DEVELOPMENT OF COAXIAL ROTOR MICRO UNMANNED AERIAL VEHICLE
- DESIGN AND TESTING OF COAXIAL ROTOR DUCTED FAN VTOL UAV
- ANALISIS LOMPAT VERTIKAL TIPE SQUAT DENGAN MODEL SISTEM BENDA JAMAK
- PENGHEMAT BAHAN BAKAR PADA KOMPOR GAS RUMAH TANGGA
- THE APPLICATION OF CONSTRAINT PROPAGATION TECHNIQUE FOR CONCEPTUAL AIRCRAFT DESIGN
- PENYELESAIAN PENDEKATAN PROBLEM KONTAK HERTZIAN PADA KASUS KONTAK ANTARA RODA DAN REL
- KAJI EKSPERIMENTAL CIRI GETARAN PADA BANTALAN ROL DENGAN PEMBEBANAN STATIK
- KAJIAN EKSPERIMENTAL SISTEM PENGAPIAN KONVENSIONAL DITINJAU DARI ASPEK PERAWATAN PREDIKTIF TERHADAP KONSUMSI BAHAN BAKAR PADA ENGINE TOYOTA KIJANG TYPE 5K
- STUDI EKSPERIMENTAL MESIN REFRIGERASI SIKLUS KOMPRESI UAP MENGGUNAKAN REFRIGERAN HIDROKARBON SUBSTITUSI R22 PADA KONDISI TRANSIENT
- ANALISIS ENERGI PADA SISTEM ROTARY KILN UNIT INDARUNG IV, PT. SEMEN PADANG
- ANALISIS SIFAT FISIK DAN KIMIA BIODIESEL DARI MINYAK JELANTAH SEBAGAI BAHAN BAKAR ALTERNATIF MOTOR DIESEL
- ANALISIS PENGENDALIAN MOTOR DC MENGGUNAKAN LOGIKA PID DENGAN MIKRO KONTROLER ATMEGA 8535
- UJI PRESTASI KERJA MESIN PEMBUATAN SANTAN KERING SISTEM SPRAY DRYING
- Review Metalurgi Las Baja Tahan Karat
- Review Pengelasan Baja dan Besi Cor Kelabu
- Kondisi Pemotongan Optimum Proses Pembubutan Keras Baja Perkakas Aisi O1 Menggunakan Pahat Keramik
- Analisa Dfa Pada Katup Pengatur Kecepatan Silinder Pneumatik (Dfa Analysis On Flow Control Valve Of Pneumatic Cylinder)
- Analisis Karakteristik Kebisingan Knalpot Komposit Pada Mobil Toyota Kijang Tipe 7K
- PENGARUH PERSEPSI MAHASISWA TENTANG VARIASI MENGAJAR DOSEN TERHADAP HASIL BELAJAR DALAM MATA KULIAH TEKNIK PERMESINAN
- PENINGKATAN PEMAHAMAN MAHASISWA TENTANG OVERHAUL MOTOR BENSIN MENGGUNAKAN INSTRUCTIONAL MATERIALS PADA MATA KULIAH PRAKTIK PERAKITAN OTOMOTIF II