PEMANFAATAN RESIN CA-ALGINAT TERMODIFIKASI DENGAN ETILENA DIAMINENA TETRAASETAT (EDTA) DALAM TAHAPAN PRAKONSENTRASI ION MN(II) BERBASIS METODE KOLOM

Abstrak: Research on modification of Ca-Alginate microcapsules with Ethylene Diamin Tetra Acetate (EDTA) and Utilization in stages pre concentration column Ion Pb based method has been done. Pre concentration method Pb metal ions is done by using the column or Off-Line method, the water sample is inserted into the column, in the elution using 1.5 M HCl, then eluat were collected and measured using Atomic Absorption Spectrophotometer. The optimum conditions in resin manufacture Ca-Alginate-EDTA is on the composition of CaCl2 1 M Na-alginate 1%, and 0.75% EDTA. The optimum conditions analytical performance of this resin microcapsules with the absorption of Pb most best at pH 8, retention capacity of 0.6546 mg / g resin, 1.5 M HCl eluent The concentration by volume Pb is 8 mL and 3 mL HCl eluen volume, analytical performance of this method good enough for Pb ion analysis is shown of the measurement value detection limit of 0.0469 mg / L level to able replicates expressed as a percentage coefficient of variance for 1:20%. this method can be applied to the analysis of metal ions Fe in water samples from the environment to the value of recoveries of> 95%, using techniques spike indicates that the sample matrix derived from Karang Mumus River and Well Water does not affect the measurement results and can be used by analysis of Pb in the sample water at trace levels.

Keywords: Preconcentration, Resin Ca-Alginate-EDTA, Pb, Spectrophotometer

Penulis: Rahma Juwita Sari, Aman Sentosa Panggabean, Erwin

Kode Jurnal: jpkimiadd160010

Artikel Terkait :

Jp Kimia dd 2016

• Profil Distribusi dan Klirens Pengkontras CT SCAN AuNP-PAMAM G4-NIMOTUZUMAB disimulasikan menggunakan Senyawa 198AuNP-PAMAM G4-NIMOTUZUMAB
• Biochar Sebagai Penyimpan Karbon, Perbaikan Sifat Tanah, dan Mencegah Pemanasan Global : Tinjauan
• Pembuatan Kertas Kraft dari Ampas Tebu (Saccaharum oficinarum) Menggunakan Metode Organosolv
• Desain Didaktis Pembelajaran Hidrolisis Didasarkan Hasil Refleksi Diri Guru Melalui Lesson Analysis
• Pengaruh Model Discovery learning Dengan Media Teka-Teki Silang Terhadap Peningkatan Hasil Belajar Siswa pada Materi Sistem Koloid
• Peningkatan Hasil Belajar Siswa dengan Media Animasi pada Materi Koloid di Kelas XI IPA3 SMAN 1 Unggul Darul Imarah Aceh Besar
• Penerapan Model Pembelajaran CIRC (Cooperative Integrated Reading and Composition) terhadap Prestasi Belajar Siswa pada Materi Minyak Bumi
• Identifikasi Pemahaman Siswa Terhadap Konsep Kelarutan dan Hasil Kali Kelarutan dengan Menggunakan Tes Diagnostik Three-Tier Multiple Choice
• KAJIAN REAKSI FENTON UNTUK DEGRADASI SENYAWA REMAZOL RED B PADA LIMBAH INDUSTRI TEKSTIL
• KAJIAN PERUBAHAN UKURAN RONGGA ZEOLIT RHO BERDASARKAN VARIASI RASIO Si/Al DAN VARIASI KATION ALKALI MENGGUNAKAN METODE MEKANIKA MOLEKULER
• PENGARUH VARIASI DAYA TERHADAP SELEKTIVITAS REAKSI SINTESIS ANALOG 2’-HIDROKSICALKON MENGGUNAKAN IRADIASI GELOMBANG MIKRO
• SINTESIS KOMPOSIT KITOSAN/TiO2 DAN PELAPISANNYA PADA PERMUKAAN SUBSTRAT TEKSTIL
• SINTESIS SENYAWA 1,4-BIS[(1-HIDROKSI-4-T-BUTIL-FENIL)-METIL]PIPERAZIN SEBAGAI ZAT ANTIOKSIDAN
• DAYA RESISTENSI Pseudomonas stutzeri TERHADAP MERKURI DAN POTENSINYA MENGHASILKAN ENZIM MERKURI REDUKTASE
• PENGARUH SUHU PEMANASAN DAN AGEN PENGIKAT DALAM PEMBUATAN KONDUKTOR LISTRIK BERBASIS ARANG
• Pembuatan Biofuel dari Palm Stearin dengan Proses Perengkahan Katalitik Menggunakan Katalis ZSM-5
• Pengaruh Penggunaan Fotokatalis TiO2/Resin, TiO2/Zeolit Dan TiO2/Karbon Aktif dalam Proses Fotoreduksi Ion Hg(II) dengan Metode SODIS (Solar Desinfection Water)
• Pengaruh Rasio Biji terhadap Pelarut dan Waktu Ekstraksi terhadap Yield dan Kualitas Minyak Biji Alpukat
• Penyisihan COD dari Limbah Cair Pabrik Minyak Kelapa Sawit menggunakan Nano Karbon Aktif
• Pengolahan Sampah Plastik Polypropylene (PP) Menjadi Bahan Bakar Minyak dengan Metode Perengkahan Katalitik Menggunakan Katalis Zeolit X
• Mesopori MCM-41 sebagai Adsorben: Kajian Kinetika dan Isotherm Adsorpsi Limbah Cair Tapioka
• Aplikasi Metode Advance Oxidation Process (AOP) Fenton pada Pengolahan Limbah Cair Pabrik Kelapa Sawit
• Evaluation of Phenol Transport Using Polymer Inclusion Membrane (PIM) with Polyeugenol as a Carrier
• Pemanfaatan Karbon Aktif dari Ampas Teh sebagai Adsorben pada Proses Adsorpsi β-Karoten yang Terkandung dalam Minyak Kelapa Sawit Mentah
• Analisis Potensi Ledakan dan Kebakaran Primary Reformer sebagai Unit Proses Produksi Amonia di PT. X