Pengaruh Tebal Potong terhadap Umur Pahat Bubut HSS yang Dilapisi Titanium dan Nitrogen dengan Teknik Sputtering DC
Abstract: To increase
performance of tool life, it can be done by superhard coating on surface of
cutting tool by using sputtering method. The research aim was to deposit
titanium and nitrogen thin film on high speed steel surface, and to
investigate the effct of depth of cut on
tool. Thin film deposition was done by
sputtering in vacuum chamber and flowed argon and nitrogen simultaneously.
Formed thin film at 27 specimens were
tested by micro hardness Vickers of 10 gf. Optimal condition of temperatures,
times and gas ratio N2:Ar of sputtering were used to coat 54 tools. Testing of tool life were done by cutting medium carbon steel by
cutting depth 0,5; 1,0; I,5 mm, feeding 0,084; 0,090; 0,112 mm/rotation and
cutting speed 23; 28; 32; 36; 42 and 48 m/min. The results show that the
optimal depth of cut of coated and uncoated tools were 1 mm, tool life and
removal material were after coated titanium and nitrogen increased at 17% dan
40,3%, respectively.
Penulis: Gusri Akhyar
Kode Jurnal: jptmesindd110312
Artikel Terkait :
Jp Teknik Mesin dd 2011
- KARAKTERISTIK PHISIK DAN STRUKTUR MIKRO KOMPOSIT LOGAM ALUMINIUM-GRAFIT HASIL PROSES METALURGI SERBUK
- ANALISIS PENENTUAN PRIORITAS VARIABEL KLASTER INDUSTRI GENTENG UNTUK PENYUSUNAN STRATEGI PENGEMBANGAN KLASTER DENGAN MENGGUNAKAN ANALISA FAKTOR (STUDI KASUS INDUSTRI GENTENG DI KAB. JEMBER)
- ANALISA TEGANGAN-REGANGAN PRODUK TONGKAT LANSIA DENGAN MENGGUNAKAN METODE ELEMEN HINGGA
- PENGEMBANGAN DAN ANALISIS ERGONOMI KURSI OPERATOR MESIN VULKANISIR BAN DENGAN METODE REVERSE ENGINEERING
- PENGARUH DIAMETER PIPA SALURAN GAS BUANG TIPE STRAIGHT THROW MUFFLER TERHADAP UNJUK KERJA MOTOR BENSIN EMPAT LANGKAH
- PENGARUH BESAR ALIRAN GAS TERHADAP CACAT POROSITAS DAN STRUKTUR MIKRO HASIL PENGELASAN MIG PADA PADUAN ALUMINIUM 5083
- ANALISA PENGARUH KARAKTERISTIK KEKUATAN PERSAINGAN PORTER TERHADAP KINERJA SEKOLAH DENGAN PENDEKATAN BALANCED SCORECARD
- PENGARUH PEMASANGAN SIRIP PENGARAH PADA BUFFER TERHADAP UNJUK KERJA MOTOR BENSIN
- STUDI PERBANDINGAN KETAHANAN KOROSI STAINLESS STEEL TIPE SS 304 DAN SS 201 MENGGUNAKAN METODE U-BEND TEST SECARA SIKLIK DENGAN VARIASI SUHU DAN PH
- Pengaruh Posisi Terhadap Kekuatan Baut dan Gaya Geser Ditinjau dari Morfologi Fracture Surface pada Sambungan Plat
- Analisis Fenomena Penampang Alir Vertical Axis Wind Turbine (VAWT) Tipe Heliks Terhadap Kecepatan Angin Sebagai Pembangkit Listrik Alternatif Berskala Rumah Tangga
- Analisis Prestasi Lampu Petromax Berbahan Bakar LPG
- Studi Perilaku Kegagalan Sambungan Las Tipe T-Conjunctions Pada Baja Karbon Rendah Dengan Pendekatan Experimen dan Numerik
- Analisis Uji Destructive Dan Non Destructive Terhadap Hasil Sambungan Las V-Tunggal Baja AISI 1045
- Studi Reduksi Beban Termal ke Dalam Ruangan Secara Konveksi dengan Sistem Underground Thermal Storage Sebagai Altenatif untuk Mendinginkan Ruangan Rumah Hunian
- Effect of Cutting Parameter Variation on Drilling of AISI 1045: Experimental and Simulation
- Pengaruh Rasio Panjang dan Diameter Pipa Suplai terhadap Unjuk Kerja Model Pompa Tanpa Motor (Hydraulic Ram Pump)
- PENGARUH JUMLAH SUDU RODA JALAN TERHADAP EFISIENSI TURBIN ALIRAN SILANG (CROSS FLOW)
- EXPERIMENTAL STUDY IMPROVEMENT OF QUALITY OF HOE ON SMALL METAL INDUSTRY IN THE DISTRIC PRINGSEWU
- TAGUCHI OPTIMIZATION METHOD FOR IDENTIFYING SURFACE ROUGHNESS
- KARAKTERISTIK ALAT PENGERING PADI SKALA LAB DENGAN MENGGUNAKAN BAHAN BAKAR SEKAM PADI
- FLUKTUASI GAYA PADA PIPA SAMBUNGAN T AKIBAT ALIRAN DUA FASA CAIR-GAS
- KEMAMPUAN BENTONIT PELET TEKAN TERAKTIVASI FISIK SEBAGAI PENGGANTI ZEOLIT DALAM MENGHEMAT KONSUMSI BAHAN BAKAR MOTOR DIESEL 4-LANGKAH
- PEMBUATAN PROGRAM PERANCANGAN TURBIN SAVONIUS TIPE-U UNTUK PEMBANGKIT LISTRIK TENAGA ANGIN