STUDI PERBANDINGAN KETAHANAN KOROSI STAINLESS STEEL TIPE SS 304 DAN SS 201 MENGGUNAKAN METODE U-BEND TEST SECARA SIKLIK DENGAN VARIASI SUHU DAN PH
Abstract: There are many
failures in a structure that is caused by the damage of the metal that support
them. One of the problem which can cause the damage of the metal is corrosion.
With its action, corrosion can make a metal
become thin, and in some cases can make a crack and fracture. Some
factors are determine how fast the process is occured in corrosion process, for
examples are the oxygen concentration, degree of acidity, and temperature. The
purpose of this research is to know how is the role of that factors in
corrrosion process. This research is implemented in three condision of
temperatures (300 C, 500 C, 700 C), variation of HCl’s pH (0, 1, 2), and cycle
environments condition. That will be combined and will be tested for about 7
days. After this execution, material will be measured for the decrease of the
weight to give the value of corrosion rate. From this experiment, the rate of
corrosion rises by increasing temperature and the decreasing pH condition. In
all condition of this experiment, the SS 304 Stainless Steel has the better
resistant to the corrosion in HCl environment.
The highest corrosion rate of cycle condition is 36.119,4 mpy for SS 201
Stainless Steel, and 515,5 mpy for SS 304 Stainless Steel. Form the micro
photographs of corrosion happened on SS 201 Stainless Steel is pitting
corrosion and SS 304 Stainless Steel is uniform corrosion.
Penulis: Sumarji
Kode Jurnal: jptmesindd110321
Artikel Terkait :
Jp Teknik Mesin dd 2011
- KARAKTERISTIK PHISIK DAN STRUKTUR MIKRO KOMPOSIT LOGAM ALUMINIUM-GRAFIT HASIL PROSES METALURGI SERBUK
- ANALISIS PENENTUAN PRIORITAS VARIABEL KLASTER INDUSTRI GENTENG UNTUK PENYUSUNAN STRATEGI PENGEMBANGAN KLASTER DENGAN MENGGUNAKAN ANALISA FAKTOR (STUDI KASUS INDUSTRI GENTENG DI KAB. JEMBER)
- ANALISA TEGANGAN-REGANGAN PRODUK TONGKAT LANSIA DENGAN MENGGUNAKAN METODE ELEMEN HINGGA
- PENGEMBANGAN DAN ANALISIS ERGONOMI KURSI OPERATOR MESIN VULKANISIR BAN DENGAN METODE REVERSE ENGINEERING
- PENGARUH DIAMETER PIPA SALURAN GAS BUANG TIPE STRAIGHT THROW MUFFLER TERHADAP UNJUK KERJA MOTOR BENSIN EMPAT LANGKAH
- PENGARUH BESAR ALIRAN GAS TERHADAP CACAT POROSITAS DAN STRUKTUR MIKRO HASIL PENGELASAN MIG PADA PADUAN ALUMINIUM 5083
- ANALISA PENGARUH KARAKTERISTIK KEKUATAN PERSAINGAN PORTER TERHADAP KINERJA SEKOLAH DENGAN PENDEKATAN BALANCED SCORECARD
- PENGARUH PEMASANGAN SIRIP PENGARAH PADA BUFFER TERHADAP UNJUK KERJA MOTOR BENSIN
- Pengaruh Posisi Terhadap Kekuatan Baut dan Gaya Geser Ditinjau dari Morfologi Fracture Surface pada Sambungan Plat
- Analisis Fenomena Penampang Alir Vertical Axis Wind Turbine (VAWT) Tipe Heliks Terhadap Kecepatan Angin Sebagai Pembangkit Listrik Alternatif Berskala Rumah Tangga
- Analisis Prestasi Lampu Petromax Berbahan Bakar LPG
- Studi Perilaku Kegagalan Sambungan Las Tipe T-Conjunctions Pada Baja Karbon Rendah Dengan Pendekatan Experimen dan Numerik
- Analisis Uji Destructive Dan Non Destructive Terhadap Hasil Sambungan Las V-Tunggal Baja AISI 1045
- Studi Reduksi Beban Termal ke Dalam Ruangan Secara Konveksi dengan Sistem Underground Thermal Storage Sebagai Altenatif untuk Mendinginkan Ruangan Rumah Hunian
- Effect of Cutting Parameter Variation on Drilling of AISI 1045: Experimental and Simulation
- Pengaruh Rasio Panjang dan Diameter Pipa Suplai terhadap Unjuk Kerja Model Pompa Tanpa Motor (Hydraulic Ram Pump)
- Pengaruh Tebal Potong terhadap Umur Pahat Bubut HSS yang Dilapisi Titanium dan Nitrogen dengan Teknik Sputtering DC
- PENGARUH JUMLAH SUDU RODA JALAN TERHADAP EFISIENSI TURBIN ALIRAN SILANG (CROSS FLOW)
- EXPERIMENTAL STUDY IMPROVEMENT OF QUALITY OF HOE ON SMALL METAL INDUSTRY IN THE DISTRIC PRINGSEWU
- TAGUCHI OPTIMIZATION METHOD FOR IDENTIFYING SURFACE ROUGHNESS
- KARAKTERISTIK ALAT PENGERING PADI SKALA LAB DENGAN MENGGUNAKAN BAHAN BAKAR SEKAM PADI
- FLUKTUASI GAYA PADA PIPA SAMBUNGAN T AKIBAT ALIRAN DUA FASA CAIR-GAS
- KEMAMPUAN BENTONIT PELET TEKAN TERAKTIVASI FISIK SEBAGAI PENGGANTI ZEOLIT DALAM MENGHEMAT KONSUMSI BAHAN BAKAR MOTOR DIESEL 4-LANGKAH
- PEMBUATAN PROGRAM PERANCANGAN TURBIN SAVONIUS TIPE-U UNTUK PEMBANGKIT LISTRIK TENAGA ANGIN