Evaluation of Phenol Transport Using Polymer Inclusion Membrane (PIM) with Polyeugenol as a Carrier
Abstract: A recovery study of
phenol with Polymer Inclusion Membranes (PIMs) needs to be evaluated to
determine values of transport kinetic parameter, level of stability, and
selectivity of the membrane. This paper describes results of the evaluation of
phenol transport using PIMs with polyeugenol as a carrier. PIMs were made by
mixing polyeugenol, dibenzylether, and polyvinylchloride in a solvent
(tetrahydrofuran) then printed in a container with diameter 4.5 cm and allowed
to vaporize for 72 hours. Further evaluation studies are conducted at pH 4.5
with various parameters, among of them are various times that were taken to
identify parameters of the transport kinetics of phenol, membrane stability,
characterization, and testing of membrane selectivity by comparing transport of
phenol with another compound, in this study chromium is used. This study
results in calculation of values of transport kinetics of membrane permeability
obtained at 8.8 x 10-5 m/s, flux value of 9.512 x 10-4 g/m2s, and diffusion
coefficient of 3.826 x 10-11 m2/s. Repeating use over three times, 48 hours,
indicates reduction in power of phenol transport by 70.81%. While selectivity
test indicates that membrane is used more selectively against phenol than
chromium metal. Based on study results, phenol transport effectiveness using
PIM with polyeugenol as carrier is 91.4% in optimum condition.
Penulis: Arifina Febriasari,
Dwi Siswanta, Agung Abadi Kiswandono, Nurul Hidayat Aprilita
Kode Jurnal: jpkimiadd160674
Artikel Terkait :
Jp Kimia dd 2016
- Profil Distribusi dan Klirens Pengkontras CT SCAN AuNP-PAMAM G4-NIMOTUZUMAB disimulasikan menggunakan Senyawa 198AuNP-PAMAM G4-NIMOTUZUMAB
- Biochar Sebagai Penyimpan Karbon, Perbaikan Sifat Tanah, dan Mencegah Pemanasan Global : Tinjauan
- Pembuatan Kertas Kraft dari Ampas Tebu (Saccaharum oficinarum) Menggunakan Metode Organosolv
- Desain Didaktis Pembelajaran Hidrolisis Didasarkan Hasil Refleksi Diri Guru Melalui Lesson Analysis
- Pengaruh Model Discovery learning Dengan Media Teka-Teki Silang Terhadap Peningkatan Hasil Belajar Siswa pada Materi Sistem Koloid
- Peningkatan Hasil Belajar Siswa dengan Media Animasi pada Materi Koloid di Kelas XI IPA3 SMAN 1 Unggul Darul Imarah Aceh Besar
- Penerapan Model Pembelajaran CIRC (Cooperative Integrated Reading and Composition) terhadap Prestasi Belajar Siswa pada Materi Minyak Bumi
- Identifikasi Pemahaman Siswa Terhadap Konsep Kelarutan dan Hasil Kali Kelarutan dengan Menggunakan Tes Diagnostik Three-Tier Multiple Choice
- KAJIAN REAKSI FENTON UNTUK DEGRADASI SENYAWA REMAZOL RED B PADA LIMBAH INDUSTRI TEKSTIL
- KAJIAN PERUBAHAN UKURAN RONGGA ZEOLIT RHO BERDASARKAN VARIASI RASIO Si/Al DAN VARIASI KATION ALKALI MENGGUNAKAN METODE MEKANIKA MOLEKULER
- PENGARUH VARIASI DAYA TERHADAP SELEKTIVITAS REAKSI SINTESIS ANALOG 2’-HIDROKSICALKON MENGGUNAKAN IRADIASI GELOMBANG MIKRO
- SINTESIS KOMPOSIT KITOSAN/TiO2 DAN PELAPISANNYA PADA PERMUKAAN SUBSTRAT TEKSTIL
- SINTESIS SENYAWA 1,4-BIS[(1-HIDROKSI-4-T-BUTIL-FENIL)-METIL]PIPERAZIN SEBAGAI ZAT ANTIOKSIDAN
- DAYA RESISTENSI Pseudomonas stutzeri TERHADAP MERKURI DAN POTENSINYA MENGHASILKAN ENZIM MERKURI REDUKTASE
- PENGARUH SUHU PEMANASAN DAN AGEN PENGIKAT DALAM PEMBUATAN KONDUKTOR LISTRIK BERBASIS ARANG
- Pembuatan Biofuel dari Palm Stearin dengan Proses Perengkahan Katalitik Menggunakan Katalis ZSM-5
- Pengaruh Penggunaan Fotokatalis TiO2/Resin, TiO2/Zeolit Dan TiO2/Karbon Aktif dalam Proses Fotoreduksi Ion Hg(II) dengan Metode SODIS (Solar Desinfection Water)
- Pengaruh Rasio Biji terhadap Pelarut dan Waktu Ekstraksi terhadap Yield dan Kualitas Minyak Biji Alpukat
- Penyisihan COD dari Limbah Cair Pabrik Minyak Kelapa Sawit menggunakan Nano Karbon Aktif
- Pengolahan Sampah Plastik Polypropylene (PP) Menjadi Bahan Bakar Minyak dengan Metode Perengkahan Katalitik Menggunakan Katalis Zeolit X
- Mesopori MCM-41 sebagai Adsorben: Kajian Kinetika dan Isotherm Adsorpsi Limbah Cair Tapioka
- Aplikasi Metode Advance Oxidation Process (AOP) Fenton pada Pengolahan Limbah Cair Pabrik Kelapa Sawit
- Pemanfaatan Karbon Aktif dari Ampas Teh sebagai Adsorben pada Proses Adsorpsi β-Karoten yang Terkandung dalam Minyak Kelapa Sawit Mentah
- Analisis Potensi Ledakan dan Kebakaran Primary Reformer sebagai Unit Proses Produksi Amonia di PT. X