SIFAT DAYA SERAP AIR DAN STABILITAS PENYERAPAN AIR HIDROGEL POLIMER KOMPOSIT
Abstract: Hydrogel polymer
composite has been synthesized by using 10L scale reactor with batch systems.
Hydrogel was synthesized by radical polymerization of a mixture of carboxy
methyl cellulose, acrylic acid and methylene bis acrylamide as crosslinker.
Hydrogel polymer composite was prepared by adding bentonite to polymer
hydrogel. Swelling ratio which indicates of water absorption of hydrogel polymer
composite was 60 g / g with a standard deviation of 6.2 %. Durability and
stability tests for water absorption of hydrogel polymer composite for 15 days
showed the swelling ratio is almost constant and hydrogel is quite stable and
not broken down quickly. Effect of temperature and salt solution on water
absorption as follow; the water absorption at higher temperatures lower than
room temperature and the water absorption from the salt solution is lower than
the water absorption of pure water. These results show the hydrogel polymer
composite is sensitive to temperature and salt solution.
Penulis: Muhamad Nasir
Kode Jurnal: jpkimiadd100248
Artikel Terkait :
Jp Kimia dd 2010
- UJI PELINDIAN SENYAWA-SENYAWA TEMBAGA DAN TIMAH HITAM SETELAH STABILISASI/SOLIDIFIKASI DENGAN SEMEN PORTLAND MENGGUNAKAN ROTARY AGITATOR
- PENERAPAN MEMBRAN MIKROFILTRASI PADA PEMURNIAN EKSTRAK KALDU KACANG HIJAU (Phaseolus radiatus L.) SEBAGAI FORTIFIKAN PRODUK MAKANAN
- AKTIVITAS ANTIDIABETES EKTRAK ETIL ASETAT DAUN PANDAN WANGI (Pandanus amaryllifolius Roxb.)
- UJI AKTIVITAS EKSTRAK DAN FRAKSINASI DAUN BRUCEA JAVANICA (Merril) SECARA INVITRO
- ISOLATION AND IDENTIFICATION OF 9-METHOXYCANTHIN-6-0NE COMPOUND FROM Eurycoma longifolia ROOTS
- PREPARATION OF MgO-CeO2 MIXED OXIDE WITH IONIC LIQUID AS CATALYST FOR DIMETHYL CARBONATE SYNTHESIS VIA TRANSESTERIFICATION
- MUNICIPAL ORGANIC WASTE AS SUBSTRATE OF BIOENERGY AND FERTILIZER PRODUCTION
- PEMANFAATAN KITIN I KITOSAN SEBAGAI BAHAN ANTI MIKROBA
- TEKNIK APLIKASI KONSORSIUM BAKTERI ENDOFITIK PENAMBAT N2 ASAL TUMBUHAN EKOSISTEM AIR HITAM KALIMANTAN TENGAH DALAM MENINGKATKAN PERTUMBUHAN DAN PENAMBATAN N2 TANAMAN PADI GOGO
- ISOLASI ENZIM HORSERADISH PEROKSIDASE (HRP) DARI KULTUR SEL DAUN ARMORACIA LAPATIFOLIA DENGAN CARA FRAKSINASI MENGGUNAKAN AMONIUM SULFAT
- ISOLASI DAN IDENTIFIKASI SENYAWA TRITERPENOID DAN ASAM 3-HIDROKSINIKOTINAT DARI EKSTRAK DIKLOROMETANA AKAR Garcinia picrorrhiza Miq
- STUDI POTENSI EKSTRAK BRUCEA JAVANICA SEBAGAI BIOAKTIF ANTIKANKER PAYUDARA TERHADAP SEL T47D
- KARAKT£RISASI SENYAWA AKTIF ANTI BAKTERI MINYAK ATSIRI BUNGA CENGKEH (Syzygium arimaticum)
- KARAKTERISASI FRAKSI AKTIF ANTIBAKTERI EKSTRAK DARI DAUN PEPE (Gymnema reticulatum Br)
- LAJU KOROSI DAN MEKANISME INHIBISI ALUMINIUM MURNI MENGGUNAKAN KALIUM DAN KALSIUM STEARAT
- EKSTRAKSI ZAT WARNA ALAMI CAMPURAN BIJI PINANG, DAUN SIRIH, GAMBIR DAN PENGARUH PENAMBAHAN KMnO4 TERHADAP PEWARNAAN KAYU JENIS ALBASIA
- ISOLASI DAN IDENTIFIKASI SENYAWA GOLONGAN TRITERPENOID DARI EKSTRAK n-EKSANA DAUN KEPUH (Sterculia foetida L.) SERTA UJI AKTIVITAS ANTIRADIKAL BEBAS
- EFEKTIVITAS SISTEM PENGOLAHAN INSTALASI PENGOLAHAN AIR LIMBAH SUWUNG DENPASAR TERHADAP KADAR BOD, COD, DAN AMONIA
- SUBKLONING GEN α-L-ARABINOFURANOSIDASE (abfA) DALAM VEKTOR EKSPRESI pYES2
- BIOSORPSI KROMIUM(VI) PADA SERAT SABUT KELAPA HIJAU (Cocos nucifera)
- AKTIVITAS ANTIJAMUR MINYAK ATSIRI RIMPANG DRINGO (Acorus calamus L.) TERHADAP JAMUR Botryodiplodia theobromae PENYEBAB BUSUK BUAH PISANG
- KANDUNGAN ALUMINIUM DALAM KALENG BEKAS DAN PEMANFAATANNYA DALAM PEMBUATAN TAWAS
- SCREENING FITOKIMIA DAN AKTIVITAS ANTIRADIKAL BEBAS EKSTRAK METANOL DAUN GAHARU (Gyrinops versteegii)
- FRAKSINASI DAN IDENTIFIKASI SENYAWA TANIN PADA DAUN BELIMBING WULUH (Averrhoa bilimbi L.)