Optimalisasi Heat Input Pengelasan Gmaw Baja A36 Melalui Pemeriksaan Hasil Las
Abstract: Welding inspection
performed on post-weld construction aims to guarantee the quality of the weld.
Inspection with NDT (non destructive test) is used to determine the damages /
defects on the surface and on the inside of the weld. This research aims to
optimize the heat input welding through NDT testing, so getting information the
quality of the weld intactly. Optimization of heat input welding is done by
changing the welding speed of the welding process with constant voltage and
current so getting heat input of 678 J / mm to 1001 J / mm. NDT testing is
conducted by visual observation, dye penetrant testing and radiographic test.
The results showed that high heat input (1001 J / mm) tend to make the weld
bead becomes concave, and low heat input (678 J / mm) tend to make less
penetration. NDT test results conclude that heat input welding of 936 J / mm,
846 J / mm and 756 J / mm meet the acceptance criteria of the standard
AWS-D1.1.
Penulis: Heri Wibowo, M. Noer
Ilman, Priyo Tri Iswanto
Kode Jurnal: jptmesindd160679
Artikel Terkait :
Jp Teknik Mesin dd 2016
- ANALISA UJI KEKERASAN BAJA VCN 150 PADA POROS BALING-BALING PISAU MESIN CRUSHER
- ANALISA UJI KEKERASAN PADA POROS BAJA ST 60 DENGAN MEDIA PENDINGIN YANG BERBEDA
- Analisa Pengaruh Penambahan Mg Pada Komposit Matrik Aluminium Remelting Piston Berpenguat Sio2 Menggunakan Metode Stir Casting Terhadap Kekerasan Dan Densitas
- Pengujian Mesin Sepeda Motor 100 Cc Menggunakan Dinamometer Generator Ac 10 Kw
- Pengaruh Tekanan Kompaksi Pressure Sintering Terhadap Ketahanan Impak Dan Kekuatan Tarik Limbah Kemasan Aluminium Foil
- PEMBUATAN BRIKET BERBAHAN DASAR SEKAM PADI DAN KANTONG PLASTIK
- ANALISA RANCANGAN SEL SURYA DENGAN KAPASITAS 50 WATT UNTUK PENERANGAN PARKIRAN UNISKA
- Eksperimental Optimasi Tipe Lekuk Sudu Pada Pompa Difungsikan Sebagai Turbin Untuk Pembangkit Listrik Tenaga Picohidro
- ANALISA KEKERASAN BAJA ST 42 DENGAN PERLAKUAN PANAS MENGGUNAKAN METODE TAGUCHI
- Pengaruh Kuat Arus Listrik Dan Laju Alir Gas Pelindung Terhadap Struktur Mikro Dan Kekuatan Tarik-Geser Sambungan Las Tig Logam Tak Sejenis Alumunium Paduan 5052-Baja Galvanis Dengan Filer Al-Si 4043
- Pemilihan Kapasitas Panas Dan Temperatur Udara Alat Penukar Kalor Shell Helical Coil Multi Tube Untuk Kebutuhan Pengering Gabah Tipe Rotari Dengan Memanfaatkan Thermal Gas Buang Mesin Diesel
- Studi Eksperimental Pengaruh Twist Ratio Terhadap Karakteristik Peningkatan Perpindahan Panas Dan Faktor Gesekan Pada Penukar Kalor Pipa Konsentrik Dengan Rectangular-Cut Twisted Tape Insert
- Pengaruh Pemasangan Exhaust Fan Di Ruang Kelas 3.8 Fakultas Teknik Untirta Terhadap Kenyamanan Thermal Yang Dihasilkan
- Pengaruh Variasi Arah Serat Komposit Berpenguat Hibrida Fiberhybrid Terhadap Kekuatan Tarik Dan Densitas Material Dalam Aplikasi Body Part Mobil
- Prilaku Korosi Sambungan Las Fsw Tak Sejenis Antara Aa5083 Dan Aa6061-T6 Dengan Variasi Putaran Tool Dalam Larutan 3,5% Nacl
- Evaluasi Sensitasi Pada Baja Tahan Karat 316 Menggunakan Alat Uji Kemampukerasan Type Jominy
- Pengaruh Sudut Kemiringan Louvered Strip Insert Susunan Backward Terhadap Karakteristik Perpindahan Panas Dan Faktor Gesekan Pada Penukar Kalor Pipa Konsentrik
- Desain Dan Analisis Kekuatan Clamp External Fixation Untuk Tulang Tibia Dengan Metode Finite Element
- Mesin Pengering Handuk Dengan Energi Listrik
- Uji Performa Filter Gas Emisi Kendaraan Bermotor Berbasis Keramik Porous Dengan Aditif Tembaga, Tio2 Dan Karbon Aktif Dalam Penurunan Kadar Gas Carbon Monoksida
- Karakterisasi Penggunaan Bahan Absorben Dan Katalis Dalam Pembuatan Material Cmc Untuk Filter Gas Buang Kendaraan Bermotor
- Desain Dan Analisis Finite Element Total Lumbar Disc Replacement
- Analisa Perlakuan Alkali Dan Pengukusan Terhadap Kuat Tarik Dan Tegangan Interfacial Serat Pelepah Salak
- PENGARUH BALL PEENING TERHADAP KEKERASAN BAJA TAHAN KARAT AISI 316L